dc.description | No presente trabalho foi realizado um estudo comparativo entre as ligas AA7050- T7451 e AA2050-T84, bem como entre as direções L-T e T-L para analisar o comportamento das ligas, quando submetidos à temperatura ambiente e criogênica. Para realizar a análise comparativa entre as ligas e entre as direções, foram utilizados corpos de prova tipo C(T) (Compacto Tension), pré-trincados em fadiga. A análise comportamental das ligas foram avaliadas através dos ensaios de tenacidade à fratura, KIC, Curva KR, fadiga, da/dN. A microestrutura foi caracterizada através da microscopia ótica, microscopia eletrônica de varredura e microscopia eletrônica de transmissão. Foi observado que na direção L-T há uma maior resistência à propagação da trinca em relação à direção T-L, no que diz respeito à Curva KR, tanto para temperatura ambiente quanto para temperatura criogênica. Quando comparou-se as duas ligas na direção L-T em temperatura ambiente, ambas apresentaram um fator de intensidade de tensão similar. Os resultados dos ensaios de fadiga mostraram que a direção T-L é mais sensível à razão de carga. Analisando os resultados entre as direções L-T e T-L, observou-se que as duas ligas apresentaram comportamento anisotrópico. | |
dc.description | A comparative study was made of the AA7050-T7451 and AA2050-T84 alloys and of the L-T and T-L directions to analyze the behavior of the alloys when subjected to room and cryogenic temperatures. The comparative analyses of the alloys and directions were performed using fatigue-precracked compact tension (CT) test specimens. The behavior of the alloys was analyzed based on fracture toughness, KIC, KR curve, fatigue, and da/dN tests. Their microstructure was characterized by optical microscopy, scanning electron microscopy and transmission electron microscopy. The KR curve indicated that resistance to crack propagation was higher in the L-T direction than in the T-L direction at both room and cryogenic temperatures. In a comparison of the two alloys in the L-T direction at room temperature, they were found to present a similar stress intensity factor. The results of the fatigue tests demonstrated that the T-L direction is more sensitive to the load ratio. An analysis of the results in the L-T and T-L directions indicated that the two alloys exhibited anisotropic behavior. | |
dc.format | application/pdf | |
dc.identifier | http://www.teses.usp.br/teses/disponiveis/18/18150/tde-24072015-173030/ | |
dc.identifier | doi:10.11606/T.18.2015.tde-24072015-173030 | |
dc.identifier.uri | http://repositorio.eesc.usp.br/handle/RIEESC/4422 | |
dc.language | pt | |
dc.publisher | Biblioteca Digital de Teses e Dissertações da USP | |
dc.publisher | Universidade de São Paulo | |
dc.publisher | Escola de Engenharia de São Carlos | |
dc.rights | Liberar o conteúdo para acesso público. | |
dc.subject | Ligas de Al | |
dc.subject | Ligas de Al-Li | |
dc.subject | Taxa de propagação da trinca | |
dc.subject | Tenacidade à fratura | |
dc.subject | Al-Li alloys | |
dc.subject | Crack propagation rate | |
dc.subject | Fracture toughness | |
dc.subject | Low temperature | |
dc.title | Análise microestrutural, tenacidade à fratura e vida em fadiga das AA7050-T7451 e AA2050-T84 (Al-Li) | |
dc.title | Microstructural analysis, fracture toughness and fatigue life of AA7050-T7451 and AA2050-T84 (Al-Li) alloys | |
dc.type | Tese de Doutorado |