Avaliação do uso da macrofibra polimérica na composição de concreto para fins estruturais

Página do item simplificado
dc.contributorUniversidade de São Paulo
dc.contributor.authorLeite, Alex Macêdo
dc.date.accessioned2020-06-22T14:58:38Z
dc.date.available2020-06-22T14:58:38Z
dc.date.issued2018-06-15
dc.description.abstractO concreto reforçado com fibras (CRF) corresponde a um material compósito formado principalmente por cimento hidráulico, agregados miúdo e graúdo, água e fibras descontínuas. A principal finalidade do reforço no concreto com fibras é o aumento da capacidade resistente pós-fissuração do compósito, que reflete no ganho de tenacidade. Tradicionalmente, as fibras de aço, por possuírem elevadas rigidez e resistência à tração, são as mais utilizadas para o reforço do concreto, enquanto que as fibras sintéticas são adotadas para controle de fissuração por retração plástica do compósito. A macrofibra polimérica se trata de uma fibra sintética estrutural que se difundiu no mercado brasileiro nos últimos anos, possuindo pouca pesquisa a respeito de seu desempenho como elemento de reforço no concreto. Diante disto, nesta pesquisa foi avaliado o uso da macrofibra polimérica na composição de concreto para fins estruturais, sendo analisado o comportamento mecânico de duas matrizes de concreto reforçado com fibras, uma convencional e a outra de alta resistência, com diferentes teores de fibra de aço e de macrofibra polimérica. Para isto, foram determinados o abatimento e a massa específica de cada concreto no estado fresco. No estado endurecido, foram realizados ensaios de absorção de água, índice de vazios, massa específica, resistência à compressão, Barcelona, tenacidade à flexão em prismas e tenacidade à punção em placas. Nas misturas com maiores teores de fibra não foi possível se obter a trabalhabilidade desejada, mesmo com a adição de superplastificante. Em alguns concretos, a macrofibra polimérica e a fibra de aço tiveram desempenhos equivalentes com relação à absorção, índice de vazios, resistência residual no Estado Limite Último (ELU) dos prismas e tenacidade das placas. O acréscimo do teor de macrofibra polimérica provocou alterações não significativas no valor do índice de vazios, da resistência residual em prismas e da tenacidade em prismas e placas. Foi encontrado uma equivalência entre os valores de tenacidade do concreto com menor teor de fibra de aço e do concreto com maior teor de macrofibra polimérica para a maioria das misturas. A macrofibra polimérica apresentou uma eficiência menor do que a fibra de aço quando utilizada no concreto destinado a pisos industriais. Além disso, o acréscimo do teor de macrofibra polimérica provocou pequenas alterações na espessura do piso industrial.
dc.description.abstractThe fiber reinforced concrete (FRC) is a composite material mainly composed of hydraulic cement, fine and coarse aggregates, water and discontinuous fibers. The main purpose of the reinforcement in the concrete with fibers is the increase of the post-cracking resistant capacity of the composite, which reflects in the toughness gain. Traditionally, steel fibers, due to their high stiffness and tensile strength, are the most used for concrete reinforcement, while synthetic fibers are used to control the plastic shrinkage cracking of the composite. The polymeric macrofiber is a structural synthetic fiber that has spread in the Brazilian market in recent years, with few researches regarding its performance as a reinforcement element in concrete. Therefore, the use of the polymeric macrofiber in the concrete composition for structural purposes was evaluated in this study and the mechanical behavior of two fiber reinforced concrete matrices, one conventional and the other with high strength, with different contents of steel fiber and polymeric macrofiber, was analyzed. For this, the slump and the specific gravity of each concrete in the fresh state were determined. In the hardened state, water absorption, voids, specific gravity, compressive strength, Barcelona, flexural toughness in prisms and punching toughness in plates tests were performed. In the mixtures with higher fiber contents it was not possible to obtain the desired workability, even with the addition of superplasticizer. In some concretes, the polymeric macrofiber and the steel fiber had equivalent performances with respect to the absorption, voids, residual strength at Ultimate Limit State (ELU) of the beams and toughness of the plates. The increase of the polymeric macrofiber content did not cause significant changes in the value of the voids, residual strength in prisms and toughness in beams and plates. An equivalence of the toughness values of the concrete with lower content of steel fiber and the concrete with higher content of polymeric macrofiber was found for the majority of the mixtures. The polymeric macrofiber was less efficient than the steel fiber when used in concrete for industrial floors. In addition, the increase of the polymeric macrofiber content caused small changes in the thickness of the industrial floor.
dc.formatapplication/pdf
dc.identifier.doi10.11606/D.18.2018.tde-23042018-094235
dc.identifier.urihttp://www.teses.usp.br/teses/disponiveis/18/18134/tde-23042018-094235/
dc.identifier.urihttp://repositorio.eesc.usp.br/handle/RIEESC/7014
dc.languagept
dc.rights.holderLeite, Alex Macêdo
dc.subjectConcreto reforçado com fibras
dc.subjectTenacidade
dc.subjectPropriedades mecânicas
dc.subjectPiso industrial
dc.subjectMacrofibra polimérica
dc.subjectMechanical properties
dc.subjectPolymeric macrofiber
dc.subjectIndustrial floor
dc.subjectFiber reinforced concrete
dc.subjectToughness
dc.titleAvaliação do uso da macrofibra polimérica na composição de concreto para fins estruturais
dc.title.alternativeEvaluation of the use of polymeric macrofiber in the concrete composition for structural purposes
dc.typeDissertação de Mestrado